E-clip system
E-clip system
Part name | Technique parameter | Technical | Remark |
E clip | Type | Dia.16mm, Dia.18mm, Dia.20mm | Application for different rail type |
Material | 60Si2MnA | Chemical composition(%): | |
60Si2CrA | Chemical composition(%): | ||
55Si2Mn | Chemical composition(%): | ||
Finish | Plain oiled, color painting, or the other required by customers | Offered as ordered | |
Hardness | 44-48HRC |
| |
Toe Load | 500-700kgf for Dia.16mm |
| |
Fatigue life | for Dia.18 is 3 millions cycles without breaking |
| |
Standard refers to | DIN17221, BS970, GB/T1222 |
| |
Shoulder | Type | UIC54, UIC60, 115RE, |
|
Material | QT500-7 | Chemical composition(%): | |
QT450-10 | Chemical composition(%): | ||
Finish | Plain oiled, or color painting |
| |
Rail pad | Type | UIC54, UIC60, BS80lbs, |
|
Material | HDPE | Density: 0.95-0.98g/cm3 | |
EVA | Density:0.95-0.98g/㎝3 | ||
Rubber | Hardness:75±5A | ||
Color | Black, or other color |
| |
Insulator | Type | UIC54, UIC60, 50kg rail, 60kg rail, |
|
Material | Reinforced Nylon 66 (PA66) | Density:1.3-1.45g/㎝3 | |
Color | Black, blue, yellow, green or other color |
|